Sintesis fotokatalis komposit SiO2/TiO2 menggunakan metode hidrotermal dan uji aktivitas fotokatalitiknya pada degradasi zat warna rhodamin B telah dilakukan. SiO2 diekstraksi dari abu ampas tebu melalui metode alkali dan presipitasi asam. TiO2 disintesis menggunakan (Ti [OCH(CH3)2]4) sebagai prekursor dengan metode sol gel. Karakterisasi material yang dihasilkan dilakukan menggunakan X-ray Diffraction (XRD), Scanning Electron Microscope-Energy Dispersive X-Ray Spectroscopy (SEM-EDX) dan Brunauer Emmet Teller (BET). TiO2 yang diperoleh memiliki fasa anatas dan SiO2 yang dihasilkan memiliki fasa kristalin. Modifikasi SiO2 pada TiO2 dapat meningkatkan luas permukaan spesifik komposit 15%-SiO2/TiO2 yang dihasilkan. Hasil uji aktivitas fotokatalitik pada degradasi zat warna rhodamin B menunjukkan komposit 15-%SiO2/TiO2 memiliki aktivitas lebih tinggi dibandingkan dengan penambahan SiO2 5% b/b, 25% b/b dan 35% b/b. Komposit 15%-SiO2/TiO2 dapat mendegradasi zat warna rhodamin B hingga 98,9% di bawah sinar UV pada kondisi optimum pH larutan zat warna = 3, massa fotokatalis 0,25 g, konsentrasi zat warna rhodamin B 5 ppm dan waktu iradiasi 120 menit. Komposit 15%-SiO2/TiO2 memiliki aktivitas lebih tinggi di bawah irradiasi sinar matahari dibandingkan dengan sinar UV. Penambahan SiO2 terbukti dapat meningkatkan aktivitas fotokatalitik TiO2 melalui peningkatan adsorpsi zat warna rhodamin B pada permukaan komposit

Synthesis of SiO2/TiO2 composite photocatalyst using the hydrothermal method and evaluation of their photocatalytic activity on the degradation of rhodamine B dye has been carried out. SiO2 was extracted from sugarcane baggase ash by the alkaline and acid precipitation methods. TiO2 was synthesized using (Ti [OCH(CH3)2]4) as a precursor by the sol gel method. The characterization of the resulting materials were conducted by using X-ray Diffraction (XRD), Scanning Electron Microscope-Energy Dispersive X-Ray Spectroscopy (SEM-EDX) and Brunauer Emmet Teller (BET). XRD data indicated that TiO2 was in anatase phase and SiO2 was in crystalline phase. Modification of TiO2 by SiO2 can enhance the specific surface area of the produced 15%-SiO2/TiO2 composite. The results of the photocatalytic activity test on the degradation of rhodamine B dye show that the 15%- SiO2/TiO2 composite has higher activity than that of 5% w/w, 25% w/w and 35%. 15%-SiO2/TiO2 composite can degrade rhodamine B dye up to 98.9% under UV light at optimum conditions the initial pH of dye solution = 3, photocatalyst mass of 0,25 g, initial concentration of rhodamine B dye 5 ppm and the irradiation time was 120 minutes. 15%-SiO2/TiO2 composite has higher photocatalytic activity under the sunlight than that of UV irradiation. The addition of SiO2 has been shown can improve the photocatalytic activity of SiO2/TiO2 composites by increasing the adsorption of rhodamine B dye on the composite surface.